分类 | PE聚乙烯 | ||
子分类 | HDPE高密度聚乙烯 | ||
品牌 | ExxonMobil | ||
型号 | HTA 108 | ||
相似型号 |
项目 | 值 | 单位 | 测试方法 |
---|---|---|---|
密度 | 0.961 | ||
熔指 | 0.7 | ||
熔点 | 127 | ||
薄膜厚度 | 25 | ||
雾度 | |||
光泽度 | |||
纵向拉伸强度 | 60 | ||
纵向断裂伸长率 | 510 | ||
吸水率 | |||
纵向正割模量 | 1200 | ||
横向拉伸强度 | 31 | ||
横向正割模量 | 1700 | ||
横向断裂伸长率 | 2 | ||
纵向撕裂强度 | 0.4 | ||
横向撕裂强度 | 8.0 | ||
落标冲击强度 | 1.2 | ||
添加剂 | 无开口剂;无爽滑剂;含热稳定剂 | ||
下载 | g/cm3 | g/10min | ℃ | ɥm | Mpa | % | Mpa | Mpa | Mpa | % | g/ɥm | g/ɥm | g/ɥm | ASTM D1709A | ASTM D792 | ASTM D1238 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D1922 | ASTM D1922 |
文档更新时间 | 2021-9-6 |