分类 | PE聚乙烯 | ||
子分类 | LLDPE线性低密度聚乙烯 | ||
品牌 | ExxonMobil | ||
型号 | Enable 2010HE | ||
相似型号 |
项目 | 值 | 单位 | 测试方法 |
---|---|---|---|
密度 | 0.920 | ||
熔指 | 1.0 | ||
熔点 | 114 | ||
薄膜厚度 | 25.4 | ||
雾度 | 7.1 | ||
光泽度 | 61 | ||
纵向拉伸强度 | 60 | ||
纵向断裂伸长率 | 520 | ||
吸水率 | |||
纵向正割模量 | 200 | ||
横向拉伸强度 | 50 | ||
横向正割模量 | 230 | ||
横向断裂伸长率 | 730 | ||
纵向撕裂强度 | 4.7 | ||
横向撕裂强度 | 22.0 | ||
落标冲击强度 | 11.0 | ||
添加剂 | 开口剂2000ppm,爽滑剂500ppm,含加工助剂和热稳定剂 | ||
下载 | g/cm3 | g/10min | ℃ | ɥm | % | % | Mpa | % | Mpa | Mpa | Mpa | % | g/ɥm | g/ɥm | g/ɥm | ASTM D1709A | ASTM D792 | ASTM D1238 | ASTM D1003 | ASTM D2457 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D882 | ASTM D1922 | ASTM D1922 |